Hot-dip galvanized (HDG)

Quality Thickness/mm Coating Coating Quantity Yield point Rp (MPa) Tensile strength Rm (MPA) Elongation A80 (in %) C % Si % Mn % P % S % Ti %
DX51D 0.30 – 4.00 Z , ZF , ZM Z50 – Z600 – 270-500 22 0.18 0.5 1.2 0.12 0.045 0.3
DX52D 0.30 – 4.00 Z , ZF , ZM Z50 – Z600 140-300 270-420 26 0.12 0.5 0.6 0.1 0.045 0.3
DX53D 0.30 – 4.00 Z , ZF , ZM Z50 – Z600 140-260 270-380 30 0.12 0.5 0.6 0.1 0.045 0.3
S220GD 0.30 – 4.00 Z , ZF , ZM Z50 – Z600 min. 220 min. 300 20 0.2 0.6 1.7 0.1 0.045 –
S250GD 0.30 – 4.00 Z , ZF , ZM Z50 – Z600 min. 250 min. 330 19 0.2 0.6 1.7 0.1 0.045 –
S280GD 0.30 – 4.00 Z , ZF , ZM Z50 – Z600 min. 280 min. 360 18 0.2 0.6 1.7 0.1 0.045 –
S320GD 0.30 – 4.00 Z , ZF , ZM Z50 – Z600 min. 320 min. 390 17 0.2 0.6 1.7 0.1 0.045 –
S350GD 0.30 – 4.00 Z , ZF , ZM Z50 – Z600 min. 350 min. 420 16 0.2 0.6 1.7 0.1 0.045 –
S390GD 0.30 – 4.00 Z , ZF , ZM Z50 – Z600 min. 390 min. 460 16 0.2 0.6 1.7 0.1 0.045 –
S420GD 0.30 – 4.00 Z , ZF , ZM Z50 – Z600 min. 420 min. 480 15 0.2 0.6 1.7 0.1 0.045 –
S450GD 0.30 – 4.00 Z , ZF , ZM Z50 – Z600 min. 450 min. 510 14 0.2 0.6 1.7 0.1 0.045 –
HX260LAD 0.30 – 4.00 Z , ZF , ZM Z50 – Z600 260-330 350-430 26 0.11 0.5 1 0.03 0.025 0.15
HX300LAD 0.30 – 4.00 Z , ZF , ZM Z50 – Z600 300-380 380-480 23 0.12 0.5 1.4 0.03 0.025 0.15
HX340LAD 0.30 – 4.00 Z , ZF , ZM Z50 – Z600 340-420 410-510 21 0.12 0.5 1.4 0.03 0.025 0.15
HX380LAD 0.30 – 4.00 Z , ZF , ZM Z50 – Z600 380-480 410-510 21 0.12 0.5 1.5 0.03 0.025 0.15

-Zinc (Z) -Galvanized

-Zinc-iron (ZF) -Galvannealed

-Zinc-magnesium (ZM) – Magnelis

Electro-Galvanized (EG)

Quality Thickness/mm Yield point Rp (MPa) Tensile strength Rm (MPA) Elongation A80 (in %) C % Mn % P % S %
DC01+ZE 0.30 – 3.00 max. 280 270-410 28 0,12 0,6 0,045 0,045
DC03+ZE 0.30 – 3.00 max. 240 270-370 34 0,1 0,45 0,035 0,035
DC04+ZE 0.30 – 3.00 max. 220 270-350 37 – – – –
HC220B+ZE 0.30 – 3.00 220-270 320-400 32 – – – –
HC260LA+ZE 0.30 – 3.00 260-330 350-430 26 – – – –
HC300LA+ZE 0.30 – 3.00 300-380 380-480 23 – – – –
HC340LA+ZE 0.30 – 3.00 340-420 410-510 21 – – – –

Cold Rolled (CR)

Quality Thickness/mm Yield point Rp (MPa) Tensile strength Rm (MPA) Elongation A80 (in %) C % Si % Mn % P % S % Ti %
DC01 0.30 – 2.50 ≤280 270 – 410 28 0,120  – 0,6 0,045 0,045 –
DC03 0.30 – 2.50 ≤240 270 – 370 34 0,100  – 0,45 0,035 0,035 –
DC04 0.30 – 2.50 ≤210 270 – 350 38 0,080  – 0,4 0,03 0,03 –
DC01EK 0.30 – 2.50 ≤270 270 – 390 30 0,080  – 0,6 0,045 0,05 –
HC260LA 0.30 – 2.50 260 – 330 350 – 430 26 0,1 0,5 1 0,12 0,03 0,15
HC300LA 0.30 – 2.50 300 – 380 380 – 480 23 0,12 0,5 1,4 0,03 0,025 0,15
HC340LA 0.30 – 2.50 340 – 420 410 – 510 21 0,12 0,5 1,5 0,03 0,025 0,15

Hot Rolled & Pickled and Oiled (HR & P+O)

Quality Thickness/mm Yield point Rp (MPa) Tensile strength Rm (MPA) Elongation A80 (in %) C % Mn % P % S % N % Cu %
S235JR 1.20 – 4.00 235 360 – 510 21 ≤ 0,17 ≤1,50 ≤ 0,035 ≤ 0,035 ≤ 0,012 ≤ 0,55
S275JR 1.20 – 4.00 275 430 – 580 19 ≤ 0,21 ≤1,50 ≤ 0,035 ≤ 0,035 ≤ 0,012 ≤ 0,55
DD11 1.20 – 4.00 170 – 340 ≤440 23 ≤ 0,12 ≤ 0,60 ≤ 0,045 ≤ 0,045 – –
DD12 1.20 – 4.00 170 – 320 ≤420 25 ≤ 0,10 ≤ 0,45 ≤ 0,035 ≤ 0,035 – –
DD13 1.20 – 4.00 170 – 310 ≤400 28 ≤ 0,08 ≤ 0,40 ≤ 0,030 ≤ 0,030 – –

Pre-Painted (PPGI)

Quality Thickness/mm Coating Quantity Yield point Rp (MPa) Tensile strength Rm (MPA) Elongation A80 (in %) C % Si % Mn % P % S % Ti %
DX51D Z50 – Z140 0.30 – 1.00 – 270-500 22 0,18 0,5 1,2 0,12 0,045 0,3
0.30 – 1.00 DX52D Z50 – Z140 140-300 270-420 26 0,12 0,5 0,6 0,1 0,045 0,3
DX53D 0.30 – 1.00 Z50 – Z140 140-260 270-380 30 0,12 0,5 0,6 0,1 0,045 0,3
S220GD 0.30 – 1.00 Z50 – Z140 min. 220 min. 300 20 0,2 0,6 1,7 0,1 0,045 –
S250GD 0.30 – 1.00 Z50 – Z140 min. 250 min. 330 19 0,2 0,6 1,7 0,1 0,045 –
S280GD 0.30 – 1.00 Z50 – Z140 min. 280 min. 360 18 0,2 0,6 1,7 0,1 0,045 –
S320GD 0.30 – 1.00 Z50 – Z140 min. 320 min. 390 17 0,2 0,6 1,7 0,1 0,045 –
HX260LAD 0.30 – 1.00 Z50 – Z140 260-330 350-430 26 0,11 0,5 1 0,03 0,025 0,15