Ποιότητες - Andriana Pagouni

Hot-dip galvanized (HDG)

Quality	Thickness/mm	Coating	Coating Quantity	Yield point Rp (MPa)	Tensile strength Rm (MPA)	Elongation A80 (in %)	C %	Si %	Mn %	P %	S %	Ti %
DX51D	0.30 – 4.00	Z, ZF, ZM	Z50–Z600	–	270-500	22	0.18	0.5	1.2	0.12	0.045	0.3
DX52D	0.30 – 4.00	Z, ZF, ZM	Z50–Z600	140-300	270-420	26	0.12	0.5	0.6	0.1	0.045	0.3
DX53D	0.30 – 4.00	Z, ZF, ZM	Z50–Z600	140-260	270-380	30	0.12	0.5	0.6	0.1	0.045	0.3
S220GD	0.30 – 4.00	Z, ZF, ZM	Z50–Z600	min. 220	min. 300	20	0.2	0.6	1.7	0.1	0.045	–
S250GD	0.30 – 4.00	Z, ZF, ZM	Z50–Z600	min. 250	min. 330	19	0.2	0.6	1.7	0.1	0.045	–
S280GD	0.30 – 4.00	Z, ZF, ZM	Z50–Z600	min. 280	min. 360	18	0.2	0.6	1.7	0.1	0.045	–
S320GD	0.30 – 4.00	Z, ZF, ZM	Z50–Z600	min. 320	min. 390	17	0.2	0.6	1.7	0.1	0.045	–
S350GD	0.30 – 4.00	Z, ZF, ZM	Z50–Z600	min. 350	min. 420	16	0.2	0.6	1.7	0.1	0.045	–
S390GD	0.30 – 4.00	Z, ZF, ZM	Z50–Z600	min. 390	min. 460	16	0.2	0.6	1.7	0.1	0.045	–
S420GD	0.30 – 4.00	Z, ZF, ZM	Z50–Z600	min. 420	min. 480	15	0.2	0.6	1.7	0.1	0.045	–
S450GD	0.30 – 4.00	Z, ZF, ZM	Z50–Z600	min. 450	min. 510	14	0.2	0.6	1.7	0.1	0.045	–
HX260LAD	0.30 – 4.00	Z, ZF, ZM	Z50–Z600	260-330	350-430	26	0.11	0.5	1	0.03	0.025	0.15
HX300LAD	0.30 – 4.00	Z, ZF, ZM	Z50–Z600	300-380	380-480	23	0.12	0.5	1.4	0.03	0.025	0.15
HX340LAD	0.30 – 4.00	Z, ZF, ZM	Z50–Z600	340-420	410-510	21	0.12	0.5	1.4	0.03	0.025	0.15
HX380LAD	0.30 – 4.00	Z, ZF, ZM	Z50–Z600	380-480	410-510	21	0.12	0.5	1.5	0.03	0.025	0.15

-Zinc (Z) -Galvanized

-Zinc-iron (ZF) -Galvannealed

-Zinc-magnesium (ZM) – Magnelis

Electro-Galvanized (EG)

Quality	Thickness/mm	Yield point Rp (MPa)	Tensile strength Rm (MPA)	Elongation A80 (in %)	C %	Mn %	P %	S %
DC01+ZE	0.30 – 3.00	max. 280	270-410	28	0.12	0.6	0.045	0.045
DC03+ZE	0.30 – 3.00	max. 240	270-370	34	0.1	0.45	0.035	0.035
DC04+ZE	0.30 – 3.00	max. 220	270-350	37	–	–	–	–
HC220B+ZE	0.30 – 3.00	220-270	320-400	32	–	–	–	–
HC260LA+ZE	0.30 – 3.00	260-330	350-430	26	–	–	–	–
HC300LA+ZE	0.30 – 3.00	300-380	380-480	23	–	–	–	–
HC340LA+ZE	0.30 – 3.00	340-420	410-510	21	–	–	–	–

Cold Rolled (CR)

Quality	Thickness/mm	Yield point Rp (MPa)	Tensile strength Rm (MPA)	Elongation A80 (in %)	C %	Si %	Mn %	P %	S %	Ti %
DC01	0.30 – 2.50	≤280	270 –410	28	0.120	–	0.6	0.045	0.045	–
DC03	0.30 – 2.50	≤240	270–370	34	0.100	–	0.45	0.035	0.035	–
DC04	0.30 – 2.50	≤210	270–350	38	0.080	–	0.4	0.03	0.03	–
DC01EK	0.30 – 2.50	≤270	270–390	30	0.080	–	0.6	0.045	0.05	–
HC260LA	0.30 – 2.50	260–330	350–430	26	0.1	0.5	1	0.12	0.03	0.15
HC300LA	0.30 – 2.50	300–380	380–480	23	0.12	0.5	1.4	0.03	0.025	0.15
HC340LA	0.30 – 2.50	340–420	410–510	21	0.12	0.5	1.5	0.03	0.025	0.15

Hot Rolled & Pickled and Oiled (HR & P+O)

Quality	Thickness/mm	Yield point Rp (MPa)	Tensile strength Rm (MPA)	Elongation A80 (in %)	C %	Mn %	P %	S %	N %	Cu %
S235JR	1.20 – 4.00	235	360–510	21	≤0.17	z1.50	≤0.035	≤0.035	≤0.012	≤0.55
S275JR	1.20 – 4.00	275	430–580	19	≤0.21	≤1.50	≤0.035	≤0.035	≤0.012	≤0.55
DD11	1.20 – 4.00	170–340	≤440	23	≤0.12	≤0.60	≤0.045	≤0.045	–	–
DD12	1.20 – 4.00	170–320	≤420	25	≤0.10	≤0.45	≤0.035	≤0.035	–	–
DD13	1.20 – 4.00	170–310	≤400	28	≤0.08	≤0.40	≤0.030	≤0.030	–	–

Pre-Painted (PPGI)

Quality	Thickness/mm	Coating Quantity	Yield point Rp (MPa)	Tensile strength Rm (MPA)	Elongation A80 (in %)	C %	Si %	Mn %	P %	S %	Ti %
DX51D	0.30 – 1.00	Z50–Z140	–	270-500	22	0.18	0.5	1.2	0.12	0.045	0.3
DX52D	0.30 – 1.00	Z50–Z140	140-300	270-420	26	0.12	0.5	0.6	0.1	0.045	0.3
DX53D	0.30 – 1.00	Z50–Z140	140-260	270-380	30	0.12	0.5	0.6	0.1	0.045	0.3
S220GD	0.30 – 1.00	Z50–Z140	min. 220	min. 300	20	0.2	0.6	1.7	0.1	0.045	–
S250GD	0.30 – 1.00	Z50-Z140	min. 250	min. 330	19	0.2	0.6	1.7	0.1	0.045	–
S280GD	0.30 – 1.00	Z50–Z140	min. 280	min. 360	18	0.2	0.6	1.7	0.1	0.045	–
S320GD	0.30 – 1.00	Z50–Z140	min. 320	min. 390	17	0.2	0.6	1.7	0.1	0.045	–
HX260LAD	0.30 – 1.00	Z50–Z140	260-330	350-430	26	0.11	0.5	1	0.03	0.025	0.15